This Standard "Nondestructive Testing of Pressure Equipments" (NB/T 47013) comprises the following 13 parts:
— Part 1: General Requirements;
— Part 2: Radiographic Testing;
— Part 3: Ultrasonic Testing;
— Part 4: Magnetic Particle Testing;
— Part 5: Penetrant Testing;
— Part 6: Eddy Current Testing;
— Part 7: Visual Testing;
— Part 8: Leak Testing;
— Part 9: Acoustic Emission Testing;
— Part 10: Ultasonic Time of Flight Diffraction Technique;
— Part 11: X-ray Digital Radioscopic Testing;
— Part 12: Magnetic Flux Leakage Testing;
— Part 13: Pulsed Eddy Current Testing.
This Part is Part 13: "Pulsed Eddy Current Testing" of NB/T 47013.
... ...
... ...
1 Scope
1.1 This Part of NB/T 47013 specifies test methods and evaluation criteria for uniform wall thickness reduction caused by corrosion, erosion or mechanical damage on ferromagnetic materials (carbon steel, low alloy steel, etc.) of pressure equipment in use, all tests shall be carried out without dismantle cover layer.
1.2 This Part is applicable to the testing of wall thickness reduction of main body base materials of pressure equipments accompanied with cover layers, which, have the following conditions:
a) Metal coating thickness not greater than 1mm;
b) For stainless steel or aluminum protective layer, cover thickness not greater than 200mm; for ferrum protective layer, cover thickness not greater than 100mm;
c) Base material thickness range is 3mm to 7mm;
d) Tube or tube fittings with diameter not less than 50mm;
e) Base material temperature range is -196℃ to 500℃.
1.3 Testing of pressure equipment in use without cover layer may refer to this Part.
2 Normative References
The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.
GB/T 12604.6 Non-destructive testing — Terminology — Terms used in eddy current testing
GB/T 28705-2012 Non-destructive testing — Test method for pulsed eddy current testing
NB/T 47013.1 Nondestructive Testing of Pressure Equipments — Part 1: General Requirements
NB/T 47013.3 Nondestructive Testing of Pressure Equipments — Part 3: Ultrasonic Testing
3 Terms and Definitions
For the purpose of this document, terms and definitions given in NB/T 47013.1, GB/T 28705, GB/T 12604.6 and the following apply.
3.1
Pulsed eddy current
The phenomenon of eddy current induced within steel body, base on the excitation of pulse magnetic field.
3.2
Parallel magnetic field
Magnetic field with exciting axial line parallel to the tangential plane of equipment surface.
3.3
Vertical magnetic field
Magnetic field with exciting axial line vertical to the tangential plane of equipment surface.
3.4
Focused mode
A kind of exciting mode, which can reduce exciting magnetic field induced in the tested workpiece with winding combination.
Foreword II
1 Scope
2 Normative References
3 Terms and Definitions
4 General Requirements
5 Testing Procedure
6 Testing Results Evaluation and Processing
7 Testing Record and Report
Appendix A (Informative) Calibration Example Drawing of Recommended Testing Point
Appendix B (Informative) Correction Relationship of Partial Recommended Testing Results
NB/T 47013.13-2015 Nondestructive testing of pressure equipments Part 13: Pulsed eddy current testing (English Version)
Standard No.
NB/T 47013.13-2015
Status
valid
Language
English
File Format
PDF
Word Count
6500 words
Price(USD)
120.0
Implemented on
2015-9-1
Delivery
via email in 1 business day
Detail of NB/T 47013.13-2015
Standard No.
NB/T 47013.13-2015
English Name
Nondestructive testing of pressure equipments Part 13: Pulsed eddy current testing
Chinese Name
承压设备无损检测 第13部分:脉冲涡流检测
Chinese Classification
Professional Classification
NB
ICS Classification
Issued by
National Energy Administration
Issued on
2015-04-02
Implemented on
2015-9-1
Status
valid
Superseded by
Superseded on
Abolished on
Superseding
Language
English
File Format
PDF
Word Count
6500 words
Price(USD)
120.0
Keywords
NB/T 47013.13-2015, NB 47013.13-2015, NBT 47013.13-2015, NB/T47013.13-2015, NB/T 47013.13, NB/T47013.13, NB47013.13-2015, NB 47013.13, NB47013.13, NBT47013.13-2015, NBT 47013.13, NBT47013.13
Introduction of NB/T 47013.13-2015
This Standard "Nondestructive Testing of Pressure Equipments" (NB/T 47013) comprises the following 13 parts:
— Part 1: General Requirements;
— Part 2: Radiographic Testing;
— Part 3: Ultrasonic Testing;
— Part 4: Magnetic Particle Testing;
— Part 5: Penetrant Testing;
— Part 6: Eddy Current Testing;
— Part 7: Visual Testing;
— Part 8: Leak Testing;
— Part 9: Acoustic Emission Testing;
— Part 10: Ultasonic Time of Flight Diffraction Technique;
— Part 11: X-ray Digital Radioscopic Testing;
— Part 12: Magnetic Flux Leakage Testing;
— Part 13: Pulsed Eddy Current Testing.
This Part is Part 13: "Pulsed Eddy Current Testing" of NB/T 47013.
... ...
... ...
1 Scope
1.1 This Part of NB/T 47013 specifies test methods and evaluation criteria for uniform wall thickness reduction caused by corrosion, erosion or mechanical damage on ferromagnetic materials (carbon steel, low alloy steel, etc.) of pressure equipment in use, all tests shall be carried out without dismantle cover layer.
1.2 This Part is applicable to the testing of wall thickness reduction of main body base materials of pressure equipments accompanied with cover layers, which, have the following conditions:
a) Metal coating thickness not greater than 1mm;
b) For stainless steel or aluminum protective layer, cover thickness not greater than 200mm; for ferrum protective layer, cover thickness not greater than 100mm;
c) Base material thickness range is 3mm to 7mm;
d) Tube or tube fittings with diameter not less than 50mm;
e) Base material temperature range is -196℃ to 500℃.
1.3 Testing of pressure equipment in use without cover layer may refer to this Part.
2 Normative References
The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.
GB/T 12604.6 Non-destructive testing — Terminology — Terms used in eddy current testing
GB/T 28705-2012 Non-destructive testing — Test method for pulsed eddy current testing
NB/T 47013.1 Nondestructive Testing of Pressure Equipments — Part 1: General Requirements
NB/T 47013.3 Nondestructive Testing of Pressure Equipments — Part 3: Ultrasonic Testing
3 Terms and Definitions
For the purpose of this document, terms and definitions given in NB/T 47013.1, GB/T 28705, GB/T 12604.6 and the following apply.
3.1
Pulsed eddy current
The phenomenon of eddy current induced within steel body, base on the excitation of pulse magnetic field.
3.2
Parallel magnetic field
Magnetic field with exciting axial line parallel to the tangential plane of equipment surface.
3.3
Vertical magnetic field
Magnetic field with exciting axial line vertical to the tangential plane of equipment surface.
3.4
Focused mode
A kind of exciting mode, which can reduce exciting magnetic field induced in the tested workpiece with winding combination.
Contents of NB/T 47013.13-2015
Foreword II
1 Scope
2 Normative References
3 Terms and Definitions
4 General Requirements
5 Testing Procedure
6 Testing Results Evaluation and Processing
7 Testing Record and Report
Appendix A (Informative) Calibration Example Drawing of Recommended Testing Point
Appendix B (Informative) Correction Relationship of Partial Recommended Testing Results