1 Scope
1.1 This standard specifies a method for determining the flexural properties of rigid and semi-rigid plastics under defined conditions. A standard test specimen is defined, but parameters are included for alternative specimen sizes for use where appropriate. A range of test speeds is included.
1.2 The method is used to investigate the flexural behaviour [1] of the test specimens and for determining the flexural strength, flexural modulus and other aspects of the flexural stress/strain relationship under the conditions defined. It applies to a freely supported beam, loaded at mid-span (three-point loading test).
1.3 The method is suitable for use with the following range of materials:
--thermoplastics moulding and extrusion materials, including filled and reinforced compounds in addition to unfilled types; rigid thermoplastics sheets;
--thermosetting moulding materials, including filled and reinforced compounds; thermosetting sheets.
In agreement with GB/T 19467.1-2004[2] and GB/T 19467.2-2004[3], this standard applies to fibre-reinforced compounds with fibre lengths≤7.5 mm prior to processing. For long-fibre-reinforced materials (laminates) with fibre lengths ＞7.5 mm, see reference [4].
The method is not normally suitable for use with rigid cellular materials and sandwich structures containing cellular material[5,6].
NOTE For certain types of textile-fibre-reinforced plastics, a four-point bending test is preferred. It is described in reference [4].
1.4 The method is peormed using specimens which may be moulded to the specified dimensions, machined from the central portion of a standard multipurpose test specimen (see GB/T 11997-2008) or machined from finished or semi-finished products such as mouldings, or extruded or cast sheet.
1.5 The method specifies preferred dimensions for the test specimen. Tests which are carried out on specimens of different dimensions, or on specimens which are prepared under different conditions, may produce results which are not comparable. Other factors, such as the test speed and the conditioning of the specimens, can also influence the results. Especially for semi-crystalline polymers, the thickness of the oriented skin layer, which is dependent on moulding conditions and thickness, affects the flexural propeies. Consequently, when comparable data are required, these factors must be carefully controlled and recorded.
Foreword I
ISO Foreword II
1 Scope
2 Normative References
3 Terms and definitions
4 Principle
5 Test Machine
6 Test Specimens
7 Conditioning
8 Procedure
9 Calculation and Expression of Results
10 Precision
11 Test Report
Annex A (Normative) Compliance Correction
Annex B (Informative) Precision Statement
Bibliography
1 Scope
1.1 This standard specifies a method for determining the flexural properties of rigid and semi-rigid plastics under defined conditions. A standard test specimen is defined, but parameters are included for alternative specimen sizes for use where appropriate. A range of test speeds is included.
1.2 The method is used to investigate the flexural behaviour [1] of the test specimens and for determining the flexural strength, flexural modulus and other aspects of the flexural stress/strain relationship under the conditions defined. It applies to a freely supported beam, loaded at mid-span (three-point loading test).
1.3 The method is suitable for use with the following range of materials:
--thermoplastics moulding and extrusion materials, including filled and reinforced compounds in addition to unfilled types; rigid thermoplastics sheets;
--thermosetting moulding materials, including filled and reinforced compounds; thermosetting sheets.
In agreement with GB/T 19467.1-2004[2] and GB/T 19467.2-2004[3], this standard applies to fibre-reinforced compounds with fibre lengths≤7.5 mm prior to processing. For long-fibre-reinforced materials (laminates) with fibre lengths ＞7.5 mm, see reference [4].
The method is not normally suitable for use with rigid cellular materials and sandwich structures containing cellular material[5,6].
NOTE For certain types of textile-fibre-reinforced plastics, a four-point bending test is preferred. It is described in reference [4].
1.4 The method is peormed using specimens which may be moulded to the specified dimensions, machined from the central portion of a standard multipurpose test specimen (see GB/T 11997-2008) or machined from finished or semi-finished products such as mouldings, or extruded or cast sheet.
1.5 The method specifies preferred dimensions for the test specimen. Tests which are carried out on specimens of different dimensions, or on specimens which are prepared under different conditions, may produce results which are not comparable. Other factors, such as the test speed and the conditioning of the specimens, can also influence the results. Especially for semi-crystalline polymers, the thickness of the oriented skin layer, which is dependent on moulding conditions and thickness, affects the flexural propeies. Consequently, when comparable data are required, these factors must be carefully controlled and recorded.
Contents of GB/T 9341-2008
Foreword I
ISO Foreword II
1 Scope
2 Normative References
3 Terms and definitions
4 Principle
5 Test Machine
6 Test Specimens
7 Conditioning
8 Procedure
9 Calculation and Expression of Results
10 Precision
11 Test Report
Annex A (Normative) Compliance Correction
Annex B (Informative) Precision Statement
Bibliography