Standard No.:	GB/T 4337-2008
English Name:	Metallic materials - Fatigue testing - Rotating bar bending method
Chinese Name:	金属材料 疲劳试验 旋转弯曲方法
Chinese Classification:	H22    Metal mechanical property test method
Professional Classification:	GB    National Standard
ICS Classification:	77.040.10 77.040.10    Mechanical testing of metals 77.040.10
Source Content Issued by:	AQSIQ; SAC
Issued on:	2008-8-5
Implemented on:	2009-4-1
Status:	superseded
Superseded by:	GB/T 4337-2015 Metallic materials―Fatigue testing―Rotating bar bending method
Superseded on:	2016-6-1
Abolished on:	2016-06-01
Superseding:	GB/T 4337-1984 Metals--Rotating bar bending fatigue testing GB/T 2107-1980 Metal material--Twisting fatigue test GB 7733-1987 Matals-rotating bar bending corrosion fatigue testing
Target Language:	English
File Format:	PDF
Word Count:	8000 words
Translation Price(USD):	240.0
Delivery:	via email in 1~3 business day

本标准规定了金属材料旋转棒弯曲疲劳试验方法。
本标准适用于金属材料在室温和高温空气中试样旋转弯曲的条件下进行的疲劳试验，其他环境（如腐蚀）下的也可参照本标准执行。
本标准代替GB/T 2107-1980《金属高温旋转弯曲疲劳试验方法》、GB/T 4337-1984《金属旋转弯曲疲劳试验方法》和GB/T 7733-1987《金属旋转弯曲腐蚀疲劳试验方法》。本标准与上述标准相比主要变化如下：
———标准的结构上发生了重大改变，本标准按照GB/T 1.1-2000重新组织了编写，由原国标的7章增加为12章，为了与国际标准一致，将原国标附录的内容更改为“旋转弯曲疲劳试验机弯距的校验”，并由资料性附录变为“规范性附录”。原国标附录中的主要内容并入本标准正文的第7章“试样制备”；
———本国标将三个原国标的范围合并，改为“本标准适用于金属材料在室温和高温空气中试样旋转
弯曲的条件下进行的疲劳试验，其他环境（如腐蚀）下的也可参照本标准执行”；
———在第４章中增加了杠杆比和力臂的定义和符号，将原国标中“条件疲劳极限”改为“耐久极限应
力”，GB/T 10623中已有的相关术语“应力比”、“疲劳寿命”、“犛犖曲线图”、“应力集中系数”
和“存活率”不再单独列出；删除了原腐蚀疲劳试验方法中关于腐蚀的术语和定义；
———在第7章与原国标相比增加了“取样和标记”、“试样的表面状态”和“尺寸检查”等新的要求。
在“7.3　加工过程”中将原国标的附录内容补充进来，另外增加了两条注；
———在第9章补充了原国标高温旋转弯曲疲劳试验的内容；
———在第10章较原国标增加了“10.2　加载”和“10.4　高温试验步骤”；
———原GB/T 7733-1987中腐蚀试验条件和腐蚀试验装置的操作未单独列出；
———增加了一个新的规范性附录Ａ“旋转弯曲疲劳试验机弯距的校验”；
———增加了图11旋转弯曲疲劳试验机的原理图、图A.1分力测量装置的示意图和图A.2力臂测量的原理图。