Codeofchina.com is in charge of this English translation. In case of any doubt about the English translation, the Chinese original shall be considered authoritative.
This standard was developed in accordance with the rules specified in GB/T 1.1-2009.
This standard combines "Hot-rolled Quality Carbon Structural Steel Sheets and Strips" (GB/T 710-2008) and "Hot-rolled Quality Carbon Structural Steel Plates Sheets and Wide Strips" (GB/T 711-2008) by amendment.
This standard replaces "Hot-rolled Quality Carbon Structural Steel Sheets and Strips" (GB/T 710-2008) and "Hot-rolled Quality Carbon Structural Steel Plates Sheets and Wide Strips" (GB/T 711-2008). Compared with GB/T 710-2008 and GB/T 711-2008, the major technical differences in this standard are as follows:
——Cancel relevant designations of rimmed steel;
——Cancel the grade of pulling edge;
Add designations 35Mn, 55Mn and 70Mn (see Table1, Table 2 and Table 3);
——Tighten control of harmful element sulfur in steel (see Table 1);
——Adjust delivery conditions of some designations (see Table 2).
This standard was proposed by China Iron & Steel Association.
This standard is under the jurisdiction of the National Technical Committee 183 on Iron and Steel of Standardization Administration of China (SAC/TC 183).
The previous editions replaced by this standard are as follows:
——GB/T 710-1988, GB/T 710-1991, GB/T 710-2008;
——GB/T 711-1985, GB/T 711-1988, GB/T 711-2008.
Contents
Foreword i
1 Scope 1
2 Normative References 1
3 Order Content 3
4 Dimension, Shape and Weight 3
5 Technical Requirements 3
6 Test Method 9
7 Inspection Rules 10
8 Packaging, Marking and Quality Certificate 10
Hot-rolled Quality Carbon Structural Steel Plates Sheets and Strips
1 Scope
This standard specifies dimension, shape, weight, technical requirements, test method, inspection rules, packing, marking and quality certificate of hot-rolled quality carbon structural steel plates/sheets and strips.
This standard is applicable to hot-rolled quality carbon structural steel plates/sheets and strips with a thickness not greater than 100mm and a width not less than 600mm (hereinafter referred to as "steel plates/sheets and strips").
2 Normative References
The following documents are essential for the application of this standard. For dated reference, just dated edition applies to this document. For undated references, the latest edition (including any amendments) applies to this document.
GB/T 222 Permissible Tolerances for Chemical Composition of Steel Products
GB/T 223.5 Steel and Iron - Determination of Acid-soluble Silicon and Total Silicon Content - Reduced Molybdosilicate Spectrophotometric Method
GB/T 223.12 Methods for Chemical Analysis of Iron, Steel and Alloy - The Sodium Carbonate Separation-diphenyl Carbazide Photometric Method for the Determination of Chromium Content
GB/T 223.19 Methods for Chemical Analysis of Iron Steel And Alloy - The Neocuproine-chloroform Extraction Photometric Method for the Determination of Copper Content
GB/T 223.23 Iron Steel and Alloy - Determination of Nickel Content - the Dimethylglyoxime Spectrophotometric Method
GB/T 223.37 Methods for Chemical Analysis of Iron Steel And Alloy- The Indophenal Blue Photometric Methods for The Determination of Nitrogen Content after Distillation Separation
GB/T 223.59 Iron Steel and Alloy - Determination of Phosphorus Content - Bismuth Phosphomolybdate Blue Spectrophotometric Method and Antimony Phosphomolybdate Blue Spectrophotometric Method
GB/T 223.64 Iron Steel and Alloyed - Determination of Manganese Content - Flame Atomic Absorption Spectrometric Method
GB/T 223.68 Methods for Chemical Analysis of Iron, Steel and Alloy - The Potassium Iodate Titration Method after Combustion in the Pipe Furnace for the Determination of Sulfur Content
GB/T 223.86 Steel and Iron - Determination of Total Carbon Content - Infrared Absorption Method after Combustion in an Induction Furnace
GB/T 224 Determination of Depth of Decarburization of Steel
GB/T 228.1 Metallic Materials - Tensile Testing - Part 2: Method of Test at Room Temperature
GB/T 229 Metallic Materials - Charpy Pendulum Impact Test Method
GB/T 232 Metallic materials - Bend test
GB/T 247 General Rule of Acceptance, Package, Mark and Certification for Steel Plates (Sheets) and Strips
GB/T 709 Dimension, Shape, Weight and Tolerances for Hot-rolled Steel Plates and Sheets
GB/T 2970 Thicker Steel Plates- Method for Ultrasonic Inspection
GB/T 2975 Steel and Steel Products - Location and Preparation of Test Pieces for Mechanical Testing
GB/T 4336 Standard Test Method for Spark Discharge Atomic Emission Spectrometric Analysis of Carbon and Low-alloy Steel (Routine Method)
GB/T 6394 Metal - Methods for Estimating the Average Grain Size
GB/T 8170 Rules of Rounding Off for Numerical Values & Expression and Judgement of Limiting Values
GB/T 13298 Inspection Methods of Microstructure for Metals
GB/T 13299 Steel - Determination of Microstructure
GB/T 17505 Steel and Steel Products - General Technical Delivery Requirements
GB/T 20123 Steel and Iron - Determination of Total Carbon and Sulfur Content Infrared Absorption Method after Combustion in an Induction Furnace (Routine Method)
Codeofchina.com is in charge of this English translation. In case of any doubt about the English translation, the Chinese original shall be considered authoritative.
This standard was developed in accordance with the rules specified in GB/T 1.1-2009.
This standard combines "Hot-rolled Quality Carbon Structural Steel Sheets and Strips" (GB/T 710-2008) and "Hot-rolled Quality Carbon Structural Steel Plates Sheets and Wide Strips" (GB/T 711-2008) by amendment.
This standard replaces "Hot-rolled Quality Carbon Structural Steel Sheets and Strips" (GB/T 710-2008) and "Hot-rolled Quality Carbon Structural Steel Plates Sheets and Wide Strips" (GB/T 711-2008). Compared with GB/T 710-2008 and GB/T 711-2008, the major technical differences in this standard are as follows:
——Cancel relevant designations of rimmed steel;
——Cancel the grade of pulling edge;
Add designations 35Mn, 55Mn and 70Mn (see Table1, Table 2 and Table 3);
——Tighten control of harmful element sulfur in steel (see Table 1);
——Adjust delivery conditions of some designations (see Table 2).
This standard was proposed by China Iron & Steel Association.
This standard is under the jurisdiction of the National Technical Committee 183 on Iron and Steel of Standardization Administration of China (SAC/TC 183).
The previous editions replaced by this standard are as follows:
——GB/T 710-1988, GB/T 710-1991, GB/T 710-2008;
——GB/T 711-1985, GB/T 711-1988, GB/T 711-2008.
Contents
Foreword i
1 Scope 1
2 Normative References 1
3 Order Content 3
4 Dimension, Shape and Weight 3
5 Technical Requirements 3
6 Test Method 9
7 Inspection Rules 10
8 Packaging, Marking and Quality Certificate 10
Hot-rolled Quality Carbon Structural Steel Plates Sheets and Strips
1 Scope
This standard specifies dimension, shape, weight, technical requirements, test method, inspection rules, packing, marking and quality certificate of hot-rolled quality carbon structural steel plates/sheets and strips.
This standard is applicable to hot-rolled quality carbon structural steel plates/sheets and strips with a thickness not greater than 100mm and a width not less than 600mm (hereinafter referred to as "steel plates/sheets and strips").
2 Normative References
The following documents are essential for the application of this standard. For dated reference, just dated edition applies to this document. For undated references, the latest edition (including any amendments) applies to this document.
GB/T 222 Permissible Tolerances for Chemical Composition of Steel Products
GB/T 223.5 Steel and Iron - Determination of Acid-soluble Silicon and Total Silicon Content - Reduced Molybdosilicate Spectrophotometric Method
GB/T 223.12 Methods for Chemical Analysis of Iron, Steel and Alloy - The Sodium Carbonate Separation-diphenyl Carbazide Photometric Method for the Determination of Chromium Content
GB/T 223.19 Methods for Chemical Analysis of Iron Steel And Alloy - The Neocuproine-chloroform Extraction Photometric Method for the Determination of Copper Content
GB/T 223.23 Iron Steel and Alloy - Determination of Nickel Content - the Dimethylglyoxime Spectrophotometric Method
GB/T 223.37 Methods for Chemical Analysis of Iron Steel And Alloy- The Indophenal Blue Photometric Methods for The Determination of Nitrogen Content after Distillation Separation
GB/T 223.59 Iron Steel and Alloy - Determination of Phosphorus Content - Bismuth Phosphomolybdate Blue Spectrophotometric Method and Antimony Phosphomolybdate Blue Spectrophotometric Method
GB/T 223.64 Iron Steel and Alloyed - Determination of Manganese Content - Flame Atomic Absorption Spectrometric Method
GB/T 223.68 Methods for Chemical Analysis of Iron, Steel and Alloy - The Potassium Iodate Titration Method after Combustion in the Pipe Furnace for the Determination of Sulfur Content
GB/T 223.86 Steel and Iron - Determination of Total Carbon Content - Infrared Absorption Method after Combustion in an Induction Furnace
GB/T 224 Determination of Depth of Decarburization of Steel
GB/T 228.1 Metallic Materials - Tensile Testing - Part 2: Method of Test at Room Temperature
GB/T 229 Metallic Materials - Charpy Pendulum Impact Test Method
GB/T 232 Metallic materials - Bend test
GB/T 247 General Rule of Acceptance, Package, Mark and Certification for Steel Plates (Sheets) and Strips
GB/T 709 Dimension, Shape, Weight and Tolerances for Hot-rolled Steel Plates and Sheets
GB/T 2970 Thicker Steel Plates- Method for Ultrasonic Inspection
GB/T 2975 Steel and Steel Products - Location and Preparation of Test Pieces for Mechanical Testing
GB/T 4336 Standard Test Method for Spark Discharge Atomic Emission Spectrometric Analysis of Carbon and Low-alloy Steel (Routine Method)
GB/T 6394 Metal - Methods for Estimating the Average Grain Size
GB/T 8170 Rules of Rounding Off for Numerical Values & Expression and Judgement of Limiting Values
GB/T 13298 Inspection Methods of Microstructure for Metals
GB/T 13299 Steel - Determination of Microstructure
GB/T 17505 Steel and Steel Products - General Technical Delivery Requirements
GB/T 20123 Steel and Iron - Determination of Total Carbon and Sulfur Content Infrared Absorption Method after Combustion in an Induction Furnace (Routine Method)
GB/T 20125 Low-alloy Steel - Determination of Multi-element Contents - Inductively Coupled Plasma Atomic Emission Spectrometric Method
GB/T 20066 Steel and Iron - Sampling and Preparation of Samples for the Determination of Chemical Composition
3 Order Content
Contract or order of procurement concluded according to this standard shall include the following information:
a) Product name (steel plate sheet or strip);
b) The number of the standard;
c) Designation;
d) Condition of delivery;
e) Dimension and accuracy;
f) Rim condition (EC or EM);
g) Weight;
h) Special requirement.
4 Dimension, Shape and Weight
Dimensions, shape, weight and tolerances of steel plates/sheets and strips shall meet the requirements stipulated in GB/T 709.
5 Technical Requirements
5.1 Designation and Chemical Composition
5.1.1 Designation and chemical composition (smelting composition) of steels shall meet the requirements in Table 1.
Contents of GB/T 711-2017
Foreword i
1 Scope
2 Normative References
3 Order Content
4 Dimension, Shape and Weight
5 Technical Requirements
6 Test Method
7 Inspection Rules
8 Packaging, Marking and Quality Certificate