Standard No.:	GB/T 4338-2006
English Name:	Metallic materials - Tensile testing at elevated temperature
Chinese Name:	金属材料 高温拉伸试验方法
Chinese Classification:	H22    Metal mechanical property test method
Professional Classification:	GB    National Standard
ICS Classification:	77.040.10 77.040.10    Mechanical testing of metals 77.040.10
Source Content Issued by:	AQSIQ; SAC
Issued on:	2006-08-16
Implemented on:	2007-1-1
Status:	superseded
Superseded by:	GB/T 228.2-2015 Metallic materials—Tensile testing—Part 2:Method of test at elevated temperature
Superseded on:	2016-6-1
Abolished on:	2016-06-01
Superseding:	GB/T 4338-1995 Metallic materials－Tensile testing at elevated temperature
Target Language:	English
File Format:	PDF
Word Count:	8000 words
Translation Price(USD):	200.0
Delivery:	via email in 1 business day

GB/T 4338-2006Metallic materials—Tensile testing at elevated temperature 1 Scope This national standard specifies terminology, definition, symbol, name, experimentation principle, test equipment, sample, test method, result treatment and test report of metallic material tensile test method at 35℃. This standard is applicable to metallic material tensile test at 35℃. 2 Normative References The following normative documents contain provision which, through reference in this text, constitute provisions of this national standard. For all the citation files that bear the dates, all the subsequent amendment documents(not including the corrected contents)or the revised edition are not applicable to this standard, yet, all parties that enter into an agreement according to this standard are encouraged to research whether the latest edition of these documents can be used. For undated references, the latest edition of the normative document referred to applies. GB/T 228 Metallic Materials - Tensile Testing at Ambient Temperature (GB/T 228—2002, eqv ISO 6892:1998) GB/T 2975 Steel and steel products--Location and preparation of test pieces for mechanical testing (GB/T 2975—1998, eqv ISO 377:1997) GB/T 8170 Rules for Rounding-off of Numerical Values GB/T 12160 Calibration of extensometers used in uniaxial testing ( GB/T 12160—2002, ISO 9513:1999,IDT) GB/T 16825.1 Verification of static uniaxial testing machines - Part 1: Tension/compression testing machines - Verification and calibration of the force-measuring system (GB/T 16825.1—2002, ISO 7500 - 1: 1999, IDT) GB/T 17600.1 Steel--Conversion of elongation values--Part 1: Carbon and low alloy steels (GB/T 17600.1—1998, eqv ISO 2566 - 1:1984) GB/T 17600.2 Steel--Conversion of elongation values--Part 2: Austenitic steels (GB/T 17600.2—1998, eqv ISO 2566 - 2:1984) JJG 141 Working Noble Metal Thermocouples JJG 351 Verification Regulation of Working Base Metal Thermocouple 3 Terminologies and Definition This standard adopts the following terminologies and definitions. 3.1 gauge length Length of parallel part to measure elongation of sample at any moment of the test. Note: paid attention to distinguish gauge length in 3.1.1 and 3.1.2. 3.1.1 original gauge length L0 Sample gauge length at room temperature prior to application of force 3.1.2 final gauge length L※ Sample gauge length at room temperature after fracture of sample 3.2 parallel length Lc Length between parallel parts of both ends and two griped parts of sample (without head sample). 3.3 Extensometer gauge length Le Length of parallel part when extensometer is used to measure extension of the sample. Extensometer gauge length can be different from L0; but it shall be more than b, d or D (see Table 1) and less than Lc. 3.4 extension Extensometer gauge length (Lc increment) at any setting moment of test period. 3.5 elongation Increment of original gauge length ( L0) at any moment of test period. 3.6 Percentage elongation Percentage between original gauge length elongation and original gauge length ( L0). 3.6.1 Percentage permanent extension When stipulated stress is applied or canceled from the sample, percentage between extensometer gauge length extension and extensometer gauge length ( Le). 3.6.2 percentage elongation after fracture A Percentage between permanent elongation (Lu- L0) of final gauge length and original gauge length (L0) ( see figure 1). 3.6.3 Percentage total elongation at fracture At

Contents Foreword 1 Scope 2 The normative references 3 Terminologies and Definition 4 Symbol and name 5 Experimentation principles 6 Test equipment 7 Samples 8 Test methods 9 Result treatments 10 Test report Annex A Annex B Annex C Annex D Annex E Annex F Annex H Annex I Annex J Annex K